DF205 Modified Melamine Glass Cloth Rigid Laminated Sheet consists of woven glass cloth impregnated and bonded with a melamine thermosetting resin, laminated under high temperature and high pressure. The woven glass cloth shall be alkali-free.
With a high mechanical and dielectric properties and excellent arc resistance, the sheet is intended for electrical equipment as insulation structural parts, where high arc resistance is required. It also passed toxic and hazardous substance detection (RoHS Report). It is equivalent to NEMA G5 sheet, MFGC201, Hgw2272.
Available thickness: 0.5mm~100mm
Available sheet size:
1500mm*3000mm、1220mm*3000mm、1020mm*2040mm,1220mm*2440mm、1000mm*2000mm and other negotiated sizes.
The Nominal Thickness and Tolerance
|
Nominal thickness, mm |
Deviation, ±mm |
Nominal thickness, mm |
Deviation, ±mm |
|
0.5 0.6 0.8 1.0 1.2 1.6 2.0 2.5 3.0 4.0 5.0 6.0 8.0 |
0.12 0.13 0.16 0.18 0.20 0.24 0.28 0.33 0.37 0.45 0.52 0.60 0.72 |
10.0 12.0 14.0 16.0 20.0 25.0 30.0 35.0 40.0 45.0 50.0 60.0 80.0 |
0.82 0.94 1.02 1.12 1.30 1.50 1.70 1.95 2.10 2.30 2.45 2.50 2.80 |
| Note: For sheets of nominal thickness not listed in this Table, the deviation shall be the same as to the next greater thickness | |||
Physical, Mechanical and Dielectric Performances
|
No. |
Properties |
Unit |
Value |
|
|
1 |
Flexural strength,perpendicular to laminations |
At room temp. |
MPa |
≥400 |
|
At 180℃±5℃ |
≥280 |
|||
|
2 |
Impact strength, Charpy, Notch |
kJ/m2 |
≥50 |
|
|
3 |
Withstand voltage, perpendicular to laminations,in transformer oil, at 90±2℃, 1min |
kV |
See the following table |
|
|
4 |
Withstand voltage, parallel to laminations,in transformer oil, at 90±2℃,1min |
kV |
≥35 |
|
|
5 |
Insulation resistance, parallel to laminations,after immersion |
Ω |
≥1.0×108 |
|
|
6 |
Dielectric dissipation factor 1MHz, after immersion |
— |
≤0.03 |
|
|
7 |
Relative permittivity, 1MHz, after immersion |
— |
≤5.5 |
|
|
8 |
Water absorption |
mg |
See the following table |
|
|
9 |
Flammability |
classification |
≥BH2 |
|
|
10 |
Thermal life, temperature index: TI |
— |
≥180 |
|
Withstand Voltage, Perpendicular to Lamination
|
Thickness, mm |
Value, KV |
Thickness, mm |
Value, KV |
|
0.5 0.6 0.7 0.8 0.9 1.0 1.2 1.4 1.6 |
9.0 11 12 13 14 16 18 20 22 |
1.8 2.0 2.2 2.4 2.5 2.6 2.8 Over 3.0
|
24 26 28 29 29 29 29 31
|
| Note: The thickness listed above is the average of test results. Sheets with thickness between two average thickness listed above, the withstand voltage (perpendicular to laminations) shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, value of withstand voltage shall be the same of 0.5mm sheet. Sheets thicker than 3mm shall be machined to 3mm on one surface before test. | |||
Water Absorption
|
Thickness, mm |
Value, mg |
Thickness, mm |
Value, mg |
|
0.5 0.6 0.8 1.0 1.2 1.5 2.0 2.5 3.0 4.0 |
≤25 ≤26 ≤27 ≤28 ≤29 ≤30 ≤32 ≤35 ≤36 ≤40 |
5.0 6.0 8.0 10.0 12.0 14.0 16.0 20.0 25.0 22.5（machined, one side） |
≤45 ≤50 ≤60 ≤70 ≤80 ≤90 ≤100 ≤120 ≤140 ≤150 |
| Note: The thickness listed above is the average of test results. Sheets with thickness between the two thickness listed above, the water absorption shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, the values shall be the same of the 0.5mm sheet. Sheets thicker than 25mm shall be machined to 22.5mm on one surface before experiment. | |||
Packing and Storage
The sheets shall be stored in a place where temperature is no higher than 40℃,and be placed evenly on a pad with a 50mm or above height.
Keep away from fire, heat (heating apparatus) and sunshine. The storage life of sheets is 18 months from the date of dispatch. If the storage life is over 18 months, the product can still be used provided being tested to be qualified.
Remarks and Precautions for Handling and Use
A high speed and small depth of cutting shall be applied when machining because of sheets’ weak thermal conductivity.
Machining and cutting this product will release much dust and smoke.
Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and use of suitable dust/particle masks is advised.
Production Equipment
The Package for Laminated Sheets
Product detail pictures:
Related Product Guide:
It can be our accountability to satisfy your preferences and competently provide you. Your satisfaction is our greatest reward. We are searching ahead towards your visit for joint growth for 100% Original Power Conversion Laminated Bus Bar - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F , The product will supply to all over the world, such as: Uganda, Portland, Zimbabwe, We welcome you to visit our company, factory and our showroom displayed various products that will meet your expectation, meanwhile, it is convenient to visit our website, our sales staff will try their efforts to offer you the best service. If you need to have more information, remember to do not hesitate to contact us by E-mail or telephone.
By Hellyngton Sato from Lithuania - 2018.09.29 17:23
As an international trading company, we have numerous partners, but about your company, I just want to say, you are really good, wide range, good quality, reasonable prices, warm and thoughtful service, advanced technology and equipment and workers have professional training, feedback and product update is timely, in short, this is a very pleasant cooperation, and we look forward to the next cooperation!
By John from Madagascar - 2018.11.02 11:11
-
OEM/ODM China Machined Insulation Parts - Cust...
-
Cheap PriceList for Frp Structure Shape - Chin...
-
Competitive Price for Dmd For Transformer - Ch...
-
Factory wholesale Epoxy Resin Fiberglass Sheets...
-
2022 wholesale price Laminated Copper Busbar -...
-
OEM/ODM Manufacturer Bear Materials Delaware -...