8 Year Exporter Laminate Composition - DF350A Modified Diphenyl Ether Glass Cloth Rigid Laminated sheet – D&F Detail:
DF350A consists of woven glass cloth impregnated with a modified diphenyl ether thermosetting resin, laminated under high temperature and pressure. The woven glass cloth shall be alkali-free and treated by KH560.
DF350A possesses good heat resistance, excellent mechanical and dielectric properties, suitable for applications in H-class electric motors or electrical equipment as insulation structural parts or components. Especially used in these electric motors or electrical equipment which require a higher mechanical performances under thermal state stress.
Available thickness: 0.5mm~200mm
Available sheet size:
1500mm*3000mm、1220mm*3000mm、1020mm*2040mm,1220mm*2440mm、1000mm*2000mm and other negotiated sizes.
The Nominal Thickness And Allowed Tolerance (mm)
| Nominal thickness | Deviation | Nominal thickness | Deviation | Nominal thickness | Deviation |
| 0.5 | +/-0.15 | 3 | +/-0.37 | 16 | +/-1.12 |
| 0.6 | +/-0.15 | 4 | +/-0.45 | 20 | +/-1.30 |
| 0.8 | +/-0.18 | 5 | +/-0.52 | 25 | +/-1.50 |
| 1 | +/-0.18 | 6 | +/-0.60 | 30 | +/-1.70 |
| 1.2 | +/-0.21 | 8 | +/-0.72 | 35 | +/-1.95 |
| 1.5 | +/-0.25 | 10 | +/-0.94 | 40 | +/-2.10 |
| 2 | +/-0.30 | 12 | +/-0.94 | 45 | +/-2.45 |
| 2.5 | +/-0.33 | 14 | +/-1.02 | 50 | +/-2.60 |
Bending Deflection (mm)
|
Thickness |
Bending deflection |
|
|
1000（Ruler length） |
500（Ruler length） |
|
|
3.0～6.0 |
≤10 |
≤2.5 |
|
6.1～8.0 |
≤8 |
≤2.0 |
|
＞8.0 |
≤6 |
≤1.5 |
Physical, Mechanical And Dielectric Properties
| No. | Properties | Unit | Standard value | Typical value | ||
| 1 | Density | g/cm3 | 1.70～1.95 | 1.9 | ||
| 2 | Flexural strength, perpendicular to laminations (Lengthwise) | At normal condition | MPa | ≥400 | 540 | |
| 180℃+/-2℃ | ≥200 | 400 | ||||
| 3 | Impact strength（Charpy, notch, lengthwise) | kJ/m2 | ≥37 | 50 | ||
| 4 | Adhesive/bond strength | N | ≥5000 | 6900 | ||
| 5 | Water absorption | mg | See next table | 11.8 | ||
| 6 | Insulation resistance, parallel to laminations | At normal condition | MΩ | ≥1.0 x 106 | 5.3 x 107 | |
| After 24h in water | ≥1.0 x 102 | 3.8 x 104 | ||||
| 7 | Dielectric dissipation factor 1MHz | – | ≤0.05 | 1.03 x 10-2 | ||
| 8 | Dielectric constant 1MHz | – | ≤5.5 | 4.7 | ||
| 9 | Breakdown voltage，parallel to laminations ( in transformer oil at 90℃+/-2℃) | kV | ≥30 | 35 | ||
| 10 | Dielectric Strength，perpendicular to laminations ( in transformer oil at 90℃+/-2℃),2mm sheet | MV/m | ≥11.8 | 18 | ||
Water Absorption
|
Average thickness of test samples (mm) |
Water absorption (mg) |
Average thickness of test samples (mm) |
Water absorption (mg) |
Average thickness of test samples (mm) |
Water absorption (mg) |
|
0.5 |
≤17 |
2.5 |
≤21 |
12 |
≤38 |
|
0.8 |
≤18 |
3.0 |
≤22 |
16 |
≤46 |
|
1.0 |
≤18 |
5.0 |
≤25 |
20 |
≤52 |
|
1.6 |
≤19 |
8.0 |
≤31 |
25 |
≤61 |
|
2.0 |
≤20 |
10 |
≤34 |
See Remarks 2 |
≤73 |
| Remarks:1) If the calculated average of measured thickness is between two thickness mentioned in this table, the values will be acquired by interpolation. If the caculated average of measured thickness is less 0.5mm, the vales will not be over 17mg. If the caculated average of measured thickness is over 25mm, the value will not be over 61mg.2) If nominal thickkness is more than 25mm,it shall be machined to 22.5mm on one side. The machined side should be smooth. | |||||
Packing And Storage
The sheets shall be stored in a place where temperature is no higher than 40℃, and be placed horizontally on a bedplate with a height of 50mm or above.
Keep away from fire, heat (heating apparatus) and direct sunshine. The storage life of sheets is 18 months from the date of leaving factory. If the storage duration is over 18 months, the product also could be used after being tested to be qualified.
Remarks and Precautions for Application
A high speed and small cutting depth shall be applied when machining because of sheets’ weak thermal conductivity.
Machining and cutting this product will release much dust and smoke. Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and using the suitable dust/particle masks are advised.
The sheets are subject to moisture after being machined, a coating of insulating vanish is recommended.
Product detail pictures:
Related Product Guide:
We always think and practice corresponding to the change of circumstance, and grow up. We aim at the achievement of a richer mind and body and the living for 8 Year Exporter Laminate Composition - DF350A Modified Diphenyl Ether Glass Cloth Rigid Laminated sheet – D&F , The product will supply to all over the world, such as: Doha, Morocco, Istanbul, Our professional engineering group will always be ready to serve you for consultation and feedback. We're able to also offer you with absolutely free samples to meet your requirements. Finest efforts will likely be produced to offer you the ideal service and goods. For anyone who is thinking about our company and merchandise, be sure to contact us by sending us emails or contact us quickly. As a way to know our merchandise and firm. lot more, you can come to our factory to find out it. We'll always welcome guests from all over the world to our business to build company relations with us. Be sure to feel free to get in touch with us for business and we believe we've been intending to share the top trading practical experience with all our merchants.
By Jack from Georgia - 2018.05.15 10:52
Speaking of this cooperation with the Chinese manufacturer, I just want to say"well dodne", we are very satisfied.
By Merry from Indonesia - 2018.06.28 19:27
-
100% Original Busbar Module - Custom rigid cop...
-
2022 Good Quality Sheet Molding - Custom molde...
-
New Arrival China Epoxy Glass Mat Laminate Epgm...
-
China Cheap price Aluminum Laminated Bus Bar -...
-
OEM Manufacturer 6640 F Class Dmd - China High...
-
Top Suppliers Cooling Techniques - China High ...