Manufacturer for Copper Laminated Flexible Shunts - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F
Manufacturer for Copper Laminated Flexible Shunts - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F Detail:
DF205 Modified Melamine Glass Cloth Rigid Laminated Sheet consists of woven glass cloth impregnated and bonded with a melamine thermosetting resin, laminated under high temperature and high pressure. The woven glass cloth shall be alkali-free.
With a high mechanical and dielectric properties and excellent arc resistance, the sheet is intended for electrical equipment as insulation structural parts, where high arc resistance is required. It also passed toxic and hazardous substance detection (RoHS Report). It is equivalent to NEMA G5 sheet, MFGC201, Hgw2272.
Available thickness: 0.5mm~100mm
Available sheet size:
1500mm*3000mm、1220mm*3000mm、1020mm*2040mm,1220mm*2440mm、1000mm*2000mm and other negotiated sizes.
The Nominal Thickness and Tolerance
|
Nominal thickness, mm |
Deviation, ±mm |
Nominal thickness, mm |
Deviation, ±mm |
|
0.5 0.6 0.8 1.0 1.2 1.6 2.0 2.5 3.0 4.0 5.0 6.0 8.0 |
0.12 0.13 0.16 0.18 0.20 0.24 0.28 0.33 0.37 0.45 0.52 0.60 0.72 |
10.0 12.0 14.0 16.0 20.0 25.0 30.0 35.0 40.0 45.0 50.0 60.0 80.0 |
0.82 0.94 1.02 1.12 1.30 1.50 1.70 1.95 2.10 2.30 2.45 2.50 2.80 |
| Note: For sheets of nominal thickness not listed in this Table, the deviation shall be the same as to the next greater thickness | |||
Physical, Mechanical and Dielectric Performances
|
No. |
Properties |
Unit |
Value |
|
|
1 |
Flexural strength,perpendicular to laminations |
At room temp. |
MPa |
≥400 |
|
At 180℃±5℃ |
≥280 |
|||
|
2 |
Impact strength, Charpy, Notch |
kJ/m2 |
≥50 |
|
|
3 |
Withstand voltage, perpendicular to laminations,in transformer oil, at 90±2℃, 1min |
kV |
See the following table |
|
|
4 |
Withstand voltage, parallel to laminations,in transformer oil, at 90±2℃,1min |
kV |
≥35 |
|
|
5 |
Insulation resistance, parallel to laminations,after immersion |
Ω |
≥1.0×108 |
|
|
6 |
Dielectric dissipation factor 1MHz, after immersion |
— |
≤0.03 |
|
|
7 |
Relative permittivity, 1MHz, after immersion |
— |
≤5.5 |
|
|
8 |
Water absorption |
mg |
See the following table |
|
|
9 |
Flammability |
classification |
≥BH2 |
|
|
10 |
Thermal life, temperature index: TI |
— |
≥180 |
|
Withstand Voltage, Perpendicular to Lamination
|
Thickness, mm |
Value, KV |
Thickness, mm |
Value, KV |
|
0.5 0.6 0.7 0.8 0.9 1.0 1.2 1.4 1.6 |
9.0 11 12 13 14 16 18 20 22 |
1.8 2.0 2.2 2.4 2.5 2.6 2.8 Over 3.0
|
24 26 28 29 29 29 29 31
|
| Note: The thickness listed above is the average of test results. Sheets with thickness between two average thickness listed above, the withstand voltage (perpendicular to laminations) shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, value of withstand voltage shall be the same of 0.5mm sheet. Sheets thicker than 3mm shall be machined to 3mm on one surface before test. | |||
Water Absorption
|
Thickness, mm |
Value, mg |
Thickness, mm |
Value, mg |
|
0.5 0.6 0.8 1.0 1.2 1.5 2.0 2.5 3.0 4.0 |
≤25 ≤26 ≤27 ≤28 ≤29 ≤30 ≤32 ≤35 ≤36 ≤40 |
5.0 6.0 8.0 10.0 12.0 14.0 16.0 20.0 25.0 22.5（machined, one side） |
≤45 ≤50 ≤60 ≤70 ≤80 ≤90 ≤100 ≤120 ≤140 ≤150 |
| Note: The thickness listed above is the average of test results. Sheets with thickness between the two thickness listed above, the water absorption shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, the values shall be the same of the 0.5mm sheet. Sheets thicker than 25mm shall be machined to 22.5mm on one surface before experiment. | |||
Packing and Storage
The sheets shall be stored in a place where temperature is no higher than 40℃,and be placed evenly on a pad with a 50mm or above height.
Keep away from fire, heat (heating apparatus) and sunshine. The storage life of sheets is 18 months from the date of dispatch. If the storage life is over 18 months, the product can still be used provided being tested to be qualified.
Remarks and Precautions for Handling and Use
A high speed and small depth of cutting shall be applied when machining because of sheets’ weak thermal conductivity.
Machining and cutting this product will release much dust and smoke.
Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and use of suitable dust/particle masks is advised.
Production Equipment
The Package for Laminated Sheets
Product detail pictures:
Related Product Guide:
We have been ready to share our knowledge of advertising and marketing worldwide and recommend you suitable products and solutions at most competitive price ranges. So Profi Tools supply you best benefit of money and we're ready to create with each other with Manufacturer for Copper Laminated Flexible Shunts - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F , The product will supply to all over the world, such as: Gambia, Hamburg, Kuwait, We have a good reputation for stable quality products, well received by customers at home and abroad. Our company would be guided by the idea of "Standing in Domestic Markets, Walking into International Markets". We sincerely hope that we could do business with customers both at home and abroad. We expect sincere cooperation and common development!
By Ruth from Kuala Lumpur - 2018.10.01 14:14
After the signing of the contract, we received satisfactory goods in a short term, this is a commendable manufacturer.
By Harriet from venezuela - 2018.06.18 19:26
-
Factory wholesale Heatpipe Heatsink - Custom c...
-
2022 China New Design Nomex Pet Flexible Insula...
-
Top Quality Busbar For Solar Battery Bank - Cu...
-
Factory Price For Fr4 Dielectric Constant - Cu...
-
Manufacturer of 19001 Iso - Custom copper foil...
-
2022 Good Quality High Temperature Epoxy Sheets...