DF205 Modified Melamine Glass Cloth Rigid Laminated Sheet consists of woven glass cloth impregnated and bonded with a melamine thermosetting resin, laminated under high temperature and high pressure. The woven glass cloth shall be alkali-free.
With a high mechanical and dielectric properties and excellent arc resistance, the sheet is intended for electrical equipment as insulation structural parts, where high arc resistance is required. It also passed toxic and hazardous substance detection (RoHS Report). It is equivalent to NEMA G5 sheet, MFGC201, Hgw2272.
Available thickness: 0.5mm~100mm
Available sheet size:
1500mm*3000mm、1220mm*3000mm、1020mm*2040mm,1220mm*2440mm、1000mm*2000mm and other negotiated sizes.
The Nominal Thickness and Tolerance
|
Nominal thickness, mm |
Deviation, ±mm |
Nominal thickness, mm |
Deviation, ±mm |
|
0.5 0.6 0.8 1.0 1.2 1.6 2.0 2.5 3.0 4.0 5.0 6.0 8.0 |
0.12 0.13 0.16 0.18 0.20 0.24 0.28 0.33 0.37 0.45 0.52 0.60 0.72 |
10.0 12.0 14.0 16.0 20.0 25.0 30.0 35.0 40.0 45.0 50.0 60.0 80.0 |
0.82 0.94 1.02 1.12 1.30 1.50 1.70 1.95 2.10 2.30 2.45 2.50 2.80 |
| Note: For sheets of nominal thickness not listed in this Table, the deviation shall be the same as to the next greater thickness | |||
Physical, Mechanical and Dielectric Performances
|
No. |
Properties |
Unit |
Value |
|
|
1 |
Flexural strength,perpendicular to laminations |
At room temp. |
MPa |
≥400 |
|
At 180℃±5℃ |
≥280 |
|||
|
2 |
Impact strength, Charpy, Notch |
kJ/m2 |
≥50 |
|
|
3 |
Withstand voltage, perpendicular to laminations,in transformer oil, at 90±2℃, 1min |
kV |
See the following table |
|
|
4 |
Withstand voltage, parallel to laminations,in transformer oil, at 90±2℃,1min |
kV |
≥35 |
|
|
5 |
Insulation resistance, parallel to laminations,after immersion |
Ω |
≥1.0×108 |
|
|
6 |
Dielectric dissipation factor 1MHz, after immersion |
— |
≤0.03 |
|
|
7 |
Relative permittivity, 1MHz, after immersion |
— |
≤5.5 |
|
|
8 |
Water absorption |
mg |
See the following table |
|
|
9 |
Flammability |
classification |
≥BH2 |
|
|
10 |
Thermal life, temperature index: TI |
— |
≥180 |
|
Withstand Voltage, Perpendicular to Lamination
|
Thickness, mm |
Value, KV |
Thickness, mm |
Value, KV |
|
0.5 0.6 0.7 0.8 0.9 1.0 1.2 1.4 1.6 |
9.0 11 12 13 14 16 18 20 22 |
1.8 2.0 2.2 2.4 2.5 2.6 2.8 Over 3.0
|
24 26 28 29 29 29 29 31
|
| Note: The thickness listed above is the average of test results. Sheets with thickness between two average thickness listed above, the withstand voltage (perpendicular to laminations) shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, value of withstand voltage shall be the same of 0.5mm sheet. Sheets thicker than 3mm shall be machined to 3mm on one surface before test. | |||
Water Absorption
|
Thickness, mm |
Value, mg |
Thickness, mm |
Value, mg |
|
0.5 0.6 0.8 1.0 1.2 1.5 2.0 2.5 3.0 4.0 |
≤25 ≤26 ≤27 ≤28 ≤29 ≤30 ≤32 ≤35 ≤36 ≤40 |
5.0 6.0 8.0 10.0 12.0 14.0 16.0 20.0 25.0 22.5（machined, one side） |
≤45 ≤50 ≤60 ≤70 ≤80 ≤90 ≤100 ≤120 ≤140 ≤150 |
| Note: The thickness listed above is the average of test results. Sheets with thickness between the two thickness listed above, the water absorption shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, the values shall be the same of the 0.5mm sheet. Sheets thicker than 25mm shall be machined to 22.5mm on one surface before experiment. | |||
Packing and Storage
The sheets shall be stored in a place where temperature is no higher than 40℃,and be placed evenly on a pad with a 50mm or above height.
Keep away from fire, heat (heating apparatus) and sunshine. The storage life of sheets is 18 months from the date of dispatch. If the storage life is over 18 months, the product can still be used provided being tested to be qualified.
Remarks and Precautions for Handling and Use
A high speed and small depth of cutting shall be applied when machining because of sheets’ weak thermal conductivity.
Machining and cutting this product will release much dust and smoke.
Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and use of suitable dust/particle masks is advised.
Production Equipment
The Package for Laminated Sheets
Product detail pictures:
Related Product Guide:
With our leading technology also as our spirit of innovation,mutual cooperation, benefits and development, we are going to build a prosperous future jointly with your esteemed company for OEM Factory for Epoxy Glass Cloth Laminated Sheets - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F , The product will supply to all over the world, such as: Argentina, Croatia, Latvia, We have more than 200 staff including experienced managers, creative designers, sophisticated engineers and skilled workers. Through hard work of all employees for the past 20 years own company grew stronger and stronger. We always apply the "client first" principle. We also always fulfill all contracts to the point and therefore enjoy excellent reputation and trust among our customers. You are very welcome to personally visit our company.We hope to start a business partnership on the basis of mutual benefit and successful development . For more information please do no hesitate to contact us..
By Genevieve from Japan - 2017.06.25 12:48
We have been engaged in this industry for many years, we appreciate the work attitude and production capacity of the company, this is a reputable and professional manufacturer.
By June from Ecuador - 2018.12.28 15:18