OEM Supply Polyester Glass Mat Laminate Sheets - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F
OEM Supply Polyester Glass Mat Laminate Sheets - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F Detail:
DF205 Modified Melamine Glass Cloth Rigid Laminated Sheet consists of woven glass cloth impregnated and bonded with a melamine thermosetting resin, laminated under high temperature and high pressure. The woven glass cloth shall be alkali-free.
With a high mechanical and dielectric properties and excellent arc resistance, the sheet is intended for electrical equipment as insulation structural parts, where high arc resistance is required. It also passed toxic and hazardous substance detection (RoHS Report). It is equivalent to NEMA G5 sheet, MFGC201, Hgw2272.
Available thickness: 0.5mm~100mm
Available sheet size:
1500mm*3000mm、1220mm*3000mm、1020mm*2040mm,1220mm*2440mm、1000mm*2000mm and other negotiated sizes.
The Nominal Thickness and Tolerance
|
Nominal thickness, mm |
Deviation, ±mm |
Nominal thickness, mm |
Deviation, ±mm |
|
0.5 0.6 0.8 1.0 1.2 1.6 2.0 2.5 3.0 4.0 5.0 6.0 8.0 |
0.12 0.13 0.16 0.18 0.20 0.24 0.28 0.33 0.37 0.45 0.52 0.60 0.72 |
10.0 12.0 14.0 16.0 20.0 25.0 30.0 35.0 40.0 45.0 50.0 60.0 80.0 |
0.82 0.94 1.02 1.12 1.30 1.50 1.70 1.95 2.10 2.30 2.45 2.50 2.80 |
| Note: For sheets of nominal thickness not listed in this Table, the deviation shall be the same as to the next greater thickness | |||
Physical, Mechanical and Dielectric Performances
|
No. |
Properties |
Unit |
Value |
|
|
1 |
Flexural strength,perpendicular to laminations |
At room temp. |
MPa |
≥400 |
|
At 180℃±5℃ |
≥280 |
|||
|
2 |
Impact strength, Charpy, Notch |
kJ/m2 |
≥50 |
|
|
3 |
Withstand voltage, perpendicular to laminations,in transformer oil, at 90±2℃, 1min |
kV |
See the following table |
|
|
4 |
Withstand voltage, parallel to laminations,in transformer oil, at 90±2℃,1min |
kV |
≥35 |
|
|
5 |
Insulation resistance, parallel to laminations,after immersion |
Ω |
≥1.0×108 |
|
|
6 |
Dielectric dissipation factor 1MHz, after immersion |
— |
≤0.03 |
|
|
7 |
Relative permittivity, 1MHz, after immersion |
— |
≤5.5 |
|
|
8 |
Water absorption |
mg |
See the following table |
|
|
9 |
Flammability |
classification |
≥BH2 |
|
|
10 |
Thermal life, temperature index: TI |
— |
≥180 |
|
Withstand Voltage, Perpendicular to Lamination
|
Thickness, mm |
Value, KV |
Thickness, mm |
Value, KV |
|
0.5 0.6 0.7 0.8 0.9 1.0 1.2 1.4 1.6 |
9.0 11 12 13 14 16 18 20 22 |
1.8 2.0 2.2 2.4 2.5 2.6 2.8 Over 3.0
|
24 26 28 29 29 29 29 31
|
| Note: The thickness listed above is the average of test results. Sheets with thickness between two average thickness listed above, the withstand voltage (perpendicular to laminations) shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, value of withstand voltage shall be the same of 0.5mm sheet. Sheets thicker than 3mm shall be machined to 3mm on one surface before test. | |||
Water Absorption
|
Thickness, mm |
Value, mg |
Thickness, mm |
Value, mg |
|
0.5 0.6 0.8 1.0 1.2 1.5 2.0 2.5 3.0 4.0 |
≤25 ≤26 ≤27 ≤28 ≤29 ≤30 ≤32 ≤35 ≤36 ≤40 |
5.0 6.0 8.0 10.0 12.0 14.0 16.0 20.0 25.0 22.5（machined, one side） |
≤45 ≤50 ≤60 ≤70 ≤80 ≤90 ≤100 ≤120 ≤140 ≤150 |
| Note: The thickness listed above is the average of test results. Sheets with thickness between the two thickness listed above, the water absorption shall be obtained by Interpolation Method. Sheets thinner than 0.5mm, the values shall be the same of the 0.5mm sheet. Sheets thicker than 25mm shall be machined to 22.5mm on one surface before experiment. | |||
Packing and Storage
The sheets shall be stored in a place where temperature is no higher than 40℃,and be placed evenly on a pad with a 50mm or above height.
Keep away from fire, heat (heating apparatus) and sunshine. The storage life of sheets is 18 months from the date of dispatch. If the storage life is over 18 months, the product can still be used provided being tested to be qualified.
Remarks and Precautions for Handling and Use
A high speed and small depth of cutting shall be applied when machining because of sheets’ weak thermal conductivity.
Machining and cutting this product will release much dust and smoke.
Suitable measures should be taken to ensure dust levels are within acceptable limits during operations. Local exhaust ventilation and use of suitable dust/particle masks is advised.
Production Equipment
The Package for Laminated Sheets
Product detail pictures:
Related Product Guide:
Our corporation insists all along the quality policy of "product top quality is base of organization survival; purchaser pleasure will be the staring point and ending of an company; persistent improvement is eternal pursuit of staff" plus the consistent purpose of "reputation very first, purchaser first" for OEM Supply Polyester Glass Mat Laminate Sheets - PIGC301 Polyimide Glass Cloth Rigid Laminated Sheets – D&F , The product will supply to all over the world, such as: Orlando, Karachi, Jordan, We have developed large markets in many countries, such as Europe and the United States, Eastern Europe and Eastern Asia. Meanwhile with the powerful predominance in persons with ability, strict production management and business concept.we constantly carry on self-innovation, technological innovation, managing innovation and business concept innovation. To follow the world markets fashion, new products are kept on researching and providing to guarantee our competitive advantage in styles, quality, price and service.
By Irene from Kazakhstan - 2017.10.13 10:47
The company account manager has a wealth of industry knowledge and experience, he could provide appropriate program according our needs and speak English fluently.
By Ellen from Czech Republic - 2018.09.12 17:18
-
New Arrival China Machining Aluminum Parts - C...
-
China Cheap price Frp Pultruded Profiles - EPG...
-
Good Wholesale Vendors Copper Strip Flexible Bu...
-
2022 wholesale price 6650 Nhn Insulation Paper ...
-
OEM Supply G11 - China High Quality Laminated ...
-
Free sample for Power Plastics Corp - Custom c...